Pengaruh Variasi Temperatur Quenching pada Aluminium Paduan AlMgSi-Fe12% terhadap Keausan

Authors

  • Wardoyo Wardoyo Universitas Proklamasi 45 Yogyakarta
  • Sumpena Sumpena Universitas Proklamasi 45 Yogyakarta

DOI:

https://doi.org/10.30588/jeemm.v2i1.528

Keywords:

wear, quenching, AlMgSi-Fe12%

Abstract

The purpose of this research is to determine the effect of heat treatment hardening of AlMgSi-Fe12% casting aluminium alloys on wear. The tests were carried out on specimens of raw materials and heat-treated specimens with variations of temperature used were 550 oC, 575 oC, 600 oC, and 625 oC, and used 15 minutes of holding time in each heat treatment, then quenching in SAE 20 oil. The method used for wear-tested was high speed ogoshi universal testing machine wear. The result had shown on raw material a specific wear rate was 2.256102E-07 mm2/kg. Test results on the specimens that have received heat treatment hardening temperature 550 oC increased the wear value decreased to 1.7471E-07 mm2/kg. In materials with temperature heat treatment, 575 oC causes wear values were increased when compared with raw material, respectively, 2,83739E-07 mm2/kg. In materials with temperature heat treatment 600 oC also causes wear values were increased when compared with raw material, respectively, 2,65105E-07 mm2/kg. Test results on the test material that has received heat treatment temperature 625 oC increased the wear value decreased to 2.16777E-07 mm2/kg.

References

Feneau, C. (2002). Non-ferrous from Ag to Zn. Belgium: Umicore.

Hamzah, M. S., & Iqbal, M. (2008). Peningkatan Ketahanan Aus Baja Karbon Rendah dengan Metode Carburizing. Jurnal SMARTek, Vol. 6(3), 169-175.

Haryono, A., & Mugroho, K. J. (2015). Analisa Perbedaan sifat Mekanik dan Struktur Mikro pada Piston Hasil Proses Pengecoran dan Tempa. Prosiding SNST ke-6 Tahun 2015. Fakultas Teknik Universitas Wahid Hasyim Semarang, 7-11.

Hirsch, J. (1997). Alluminium Alloy for Automotive Application. Materials Science Forum, Vol. 242, 33-50.

Hutchings, I., & Shipway, P. (2017). Tribology: Friction and Wear of Engineering Materials. UK: Butterworth-Heinemann.

Koswara, E. (1999). Pengujian Bahan Logam. Bandung: Humaniora Utama Press.

Lee, J. A. (2003). Cast Aluminum Alloy for High Temperature Applications. USA: NASA-Marshall Space Flight Center.

Liang, Z. (2012). Clustering and Precipitation in Al-Mg-Si Alloys. Berlin: genehmigte Disertation. Institut fur Angewandte Materialforschung. pp. 2-12.

Nayak, S., & Anand K. K. V. N. B. (2011). Synthesis of Al-Si alloys and study of their mechanical properties. BTech thesis Department of Metallurgical and Materials Engineering, National Institute of Technology Rourkela. pp. 9-37.

Soekrisno. 2004. Perbandingan kekerasan, struktur mikro dan komposisi kimia bantalan bola produk Jepang dan China. Jurnal Mesin dan Industri, 1(3): 914.

Sriwardani, N. (2009). Heat Treatment Process. Surakarta: UNS Press.

Surdia, T., & Chijiwa, K. (1982). Teknik Pengecoran Logam. Jakarta: Pradnya Paramita.

Surdia, T., & Saito, S. (2005). Pengetahuan Bahan Teknik. (Cetakan 6). Jakarta: Pradnya Paramita.

Surono, B., & Novri, M. (2011) Perubahan Nilai Kekerasan Dan Struktur Mikro (Al-Mg-Si) Akibat Variasi Temperatur Pemanasan. Jakarta: Bina Teknika.

Syafa’at, I. (2008). Tribologi, Daerah Pelumasan Dan Keausan. Jurnal Ilmiah Momentum, Vol. 4(2), 21-26.

Saputro, T. A. (2014). Analisa Heat Treatment Pada Aluminium Magnesium Silikon (Al-Mg-Si) Dengan Silikon (Si) (1%, 3%, 5%) Terhadap Sifat Fisis Dan Mekanis. Skripsi Jurusan Teknik Mesin, Fakultas Teknik, Universitas Muhamadiyah Surakarta.

Raharjo, W. P. (2008). Pengaruh Perlakuan Panas Terhadap Struktur Mikro Dan Kekerasan Coran Paduan Al-Mg-Si. Mekanika: Mechanical Engineering Scientific Magazine, Vol 7(1), 28-35.

Wibowo, T. N., Iswanto, P. T., Priyambodo, B. H., & Amin, N. (2016). Pengaruh Variasi Waktu Shot Peening Terhadap Struktur Mikro dan Kekerasan Permukaan pada Material Implan AISI 304. Jurnal Rotor: Teknik Mesin Universitas Jember, Special Edition, 70-73.

Downloads

Published

2018-05-19

How to Cite

Wardoyo, W., & Sumpena, S. (2018). Pengaruh Variasi Temperatur Quenching pada Aluminium Paduan AlMgSi-Fe12% terhadap Keausan. Jurnal Engine: Energi, Manufaktur, Dan Material, 2(1), 33–39. https://doi.org/10.30588/jeemm.v2i1.528

Issue

Vol. 2 No. 1 (2018)

Section

Articles

License

Authors who publish with Jurnal Engine: Energi, Manufaktur, dan Material agree to the following terms: 

Authors retain copyright and grant the Jurnal Engine: Energi, Manufaktur, dan Material right of first publication with the work simultaneously licensed under a Creative Commons Attribution 4.0 International License that allows others to share (copy and redistribute the material in any medium or format) and adapt (remix, transform, and build upon the material) the work for any purpose, even commercially with an acknowledgment of the work's authorship and initial publication in Jurnal Engine: Energi, Manufaktur, dan Material. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in Jurnal Engine: Energi, Manufaktur, dan Material. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).

Most read articles by the same author(s)