Pengaruh Shot Peening terhadap Laju Perambatan Retak Fatik Sambungan Friction Stir Welding pada Aluminium Seri 5083
DOI:
https://doi.org/10.30588/jeemm.v4i1.728Keywords:
shot peening, aluminum alloy 5083, fatigue crack propagation, friction stir welding, paduan aluminium 5083, perambatan retak fatikAbstract
This research aims to find out the effect of shot peening on the rate of fatigue crack propagation in the aluminum alloy 5083, which has undergone the friction stir welding (FSW) process. In general, the FSW welded joint is subjected to softening and decreasing mechanical properties compared to the parent metal. Shot peening treatment is expected to reduce the rate of fatigue crack propagation. The FSW process is carried out on 3 mm thick aluminum and butt joint welding joints. The machine used in the FSW process is a milling machine with a spindle rotation of 910 rpm and a table speed of 18.2 mm/min. The surface of the material that has been processed by FSW, then proceeds with the shot peening process by firing steel balls for 6 minutes, 10 minutes, and 14 minutes. The results of the FSW process without shot peening (NP) and FSW with shot peening (SP) microstructure, SEM, and fatigue crack propagation tests were performed. The test results show that the FSW process with shot peening has decreased the rate of fatigue crack propagation marked by an increase in the value of the Paris constant (n). The increase in Paris's constant values (n) in the FSW with SP6, SP10, and SP14 was 0.241%, 5.428%, and 13.371%, respectively.References
Abrianto. (2007). Kelelahan Logam. Bandung: Teknik Metalurgi, Universitas Jenderal Achmad Yani.
Bradley, G. R., & James, M. N. (2000). “Geometry and Microstructure of Metal Inert Gas and Frictioan Stir Welded Aluminium Alloy 5383-H321”.
Faqih, I. A., Ma'arif, S., & Sukarjo, H. (2019). The Effect of Current Variation on MMA Welding to Mechanical Properties and Microstructure of Mild Steel. Proceeding International Conference on Materials Science and Technology (pp. 21-26). Serpong: Center for Science and Technology of Advanced Materials - BATAN.
Ishak. (2011). Pengaruh Sandblasting dan Electropolishing Terhadap Kekasaran Permukaan, Kekerasan, Struktur Mikro dan Ketahanan Korosi Baja Tahan Karat AISI 316 L. Yogyakarta: Tesis S2 Teknik Mesin, Universitas Gadjah Mada.
Jatimurti, W., Kurniawan, F., & Kurniawan, B. A. (2019). Analisa Kecepatan Pengelasan dan Kecepatan Putar Mata Pahat terhadap Konduktivitas Listrik Sambungan Aluminium dan Tembaga Hasil Friction Stir Welding (FSW). Jurnal Engine: Energi, Manufaktur, dan Material, 3(2), 39-46.
Maarif, S., Pani, R. S., Chamim, M., & Sukarjo, H. (2019). Prediction of Distortion Behavior due to Load Thermal Laser Welded Low Carbon Steel with Stainless Steel 304 Based on Computation Simulation. Proceeding International Conference on Materials Science and Technology (pp. 72-79). Serpong: Center for Science and Technology of Advanced Materials - BATAN.
Mandal, N. R. (2005). Aluminum Welding (2nd ed.). New Delhi: Narosa Publishing House.
Muchtar, K. K. (2002). Pengaruh Shot Peening Ulang Terhadap Kelelahan (Fatigue) Sambungan Las. Jurnal Teknik Mesin, 2(1), 1-6.
Sano, Y., Masaki, K., Gushi, T., & Sano, T. (2012). Improvement in fatigue performance of friction stir welded A6061-T6 aluminium alloy by laser peening without coating. Material & Design, 36, 809-814.
Sugiyanto, S., & Prabowo, Y. (2018). Pembuatan Kekasaran Permukaan Material ST 37 terhadap Kecepatan Pemakanan pada Milling Machine. Jurnal Engine: Energi, Manufaktur, dan Material, 2(1), 1-6.
Thomas, W. M. (1991). U.S. Patent No. PCT/GB92/02203. Friction Stir Butt Welding.
Wartono, W., Taufiq, M., & Julius, A. (2019). Pengaruh Preheat terhadap Sifat Mekanis Sambungan Metal Inert Gas (MIG) pada Baja Karbon Rendah. Jurnal Engine: Energi, Manufaktur, dan Material, 3(1), 15-22.
Wisnujati, A., & Nurhuda, A. (2017). Analisis Sifat Fisik dan Mekanik Sambungan Las Oxy-Acetylene pada Pelat Baja Karbon Rendah dengan Variabel Nyala Torch Karburasi. Jurnal Engine: Energi, Manufaktur, dan Material, 1(2), 1-7.
Downloads
Published
How to Cite
Issue
Section
License
Authors who publish with Jurnal Engine: Energi, Manufaktur, dan Material agree to the following terms:
Authors retain copyright and grant the Jurnal Engine: Energi, Manufaktur, dan Material right of first publication with the work simultaneously licensed under a Creative Commons Attribution 4.0 International License that allows others to share (copy and redistribute the material in any medium or format) and adapt (remix, transform, and build upon the material) the work for any purpose, even commercially with an acknowledgment of the work's authorship and initial publication in Jurnal Engine: Energi, Manufaktur, dan Material. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in Jurnal Engine: Energi, Manufaktur, dan Material. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).